The Kimya TPC-91A 3D filament belongs to the thermoplastic copolyester family: is an elastomer. TPC is an elastomer obtained by copolymerization of two types of monomers: an ester (a rigid segment) and an ether (a flexible segment). It offers chemical and impact resistance. It provides Shore hardness of 91 A. It can be used to produce flexible parts. The Kimya TPC-91A 3D filament can be used in industrial applications in sectors such as electronics, textiles, roofing, etc., and in decorative and leisure 3D printing applications. It offers the following properties:
Flexibility
Easy to print
Elongation > 500%
Complies with the REACH standard
Our Priced to Sell items come from our end-of-life inventory. Once they’re gone, they’re gone! Because these products are deeply discounted, all sales are final, and we’re not able to accept returns, exchanges, or refunds.
Filament Properties
PROPERTIES
TEST METHODS
VALUES
Diameter
INS-6712
1.75 ± 0.1 mm 2.85 ± 0.1 mm
Density
ISO 1183-1
1.22 g/cm3
Moisture rate
INS-6711
< 0.5%
Melt flow index (MFI)
ISO 1133-1 (@210°C - 2,16 kg)
18 - 20 g/10min
Melting Temperature (Tm)
ISO 11357-1 DSC (10°C/min - 20-220°C)
160°C
Print Parameters and Specimens Dimensions
PARAMETER
VALUE
Printing Direction
XY
Printing Speed
44 mm/s
Infill
100% - rectilinear
Infill Angle
45°/-45°
Nozzle Temperature
260°C
Bed Temperature
60°C
Printed Specimens Properties
PROPERTIES
TEST METHODS
VALUES
MECHANICAL PROPERTIES
Tensile modulus
ISO 37/2/500
67 MPa
Tensile Strength
ISO 37/2/500
17.7 MPa
Tensile strain at strength
ISO 37/2/500
0%
Tensile Stress at Break
ISO 37/2/500
17.5 MPa
Tensile strain at break (type A)
ISO 37/2/500
0%
Flexural modulus
ISO 178
66 MPa
Flexural stress at conventional deflection (3.5% strain)*
ISO 178
2.6 MPa
Charpy impact resistance
ISO 179-1/1eA
No Break
Shore Hardness
ISO 868
91A
Note 1:According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2:The data should be considered as indicative values - Properties can be influenced by production.